Magnetic Behavior of the Alloy (CuInTe2)1- X (TaTe)X with X = 0.25

Magnetic Behavior of the Alloy (CuInTe2)1- X (TaTe)X with X = 0.25

The magnetic behavior of the alloy (CuInTe2)1-x (TaTe)x with x = 0.25 had been studied using SQUID techniques. Measurements of DC magnetic susceptibility using the ZFC-FC protocol and variation of magnetization as a function of the applied magnetic field and temperature were performed. It was found...

Resumo completo

Bibliografia

Guardado em:
Título traduzido: Comportamiento Magnético de la Aleación (CuInTe2)1-X (TaTe)X con X = 0.25
Título da revista: Revista Cubana de Física
Primer autor: P. Grima Gallardo
Outros autores: O Izarra;
R Peña;
M. Muñoz;
S Durán;
M Quintero;
E Quintero;
H Romero
Idioma: Inglês
Ligação recurso: http://www.revistacubanadefisica.org/index.php/rcf/article/view/RCF_32-01_9-14_2015
Tipo de recurso: Artigo de revista
Fonte: Revista Cubana de Física; Vol 32, No 1 (Ano 2015).
Entidade editora: Universidad de La Habana
Direitos de utilização: Reconocimiento - NoComercial (by-nc)
Matérias: Ciências Físicas e Engenharia --> Astronomia e Astrofísica
Ciências Físicas e Engenharia --> Física
Resumo: The magnetic behavior of the alloy (CuInTe2)1-x (TaTe)x with x = 0.25 had been studied using SQUID techniques. Measurements of DC magnetic susceptibility using the ZFC-FC protocol and variation of magnetization as a function of the applied magnetic field and temperature were performed. It was found the presence of magnetic nanoclusters with a mean diameter of 10 nm and a coercitive field of 0.1 KOe at T = 5 K.
Resumo traduzido: El comportamiento magnético de la aleación (CuInTe2)1-x (TaTe)x con x = 0.25 fue estudiado utilizando la técnica de SQUID. Se midió la susceptibilidad magnética DC utilizando el protocolo ZFC-FC y la variación de la magnetización en función del campo magnético aplicado y la temperatura. Se encontró la formación de nanoclústeres magnéticos con un diámetro promedio de 10 nm y un campo coercitivo de 0.1 KOe a T = 5K.

Exemplares similares