SYNTHESIS, CRYSTAL STRUCTURE AND MAGNETIC BEHAVIOR OF C­uCo2InTe4 AND CuNi2InTe4(SÍNTESIS, ESTRUCTURA CRISTALINA Y COMPORTAMIENTO MAGNÉTICO DE CuCo2InTe4 Y CuNi2InTe4)

SYNTHESIS, CRYSTAL STRUCTURE AND MAGNETIC BEHAVIOR OF C­uCo2InTe4 AND CuNi2InTe4(SÍNTESIS, ESTRUCTURA CRISTALINA Y COMPORTAMIENTO MAGNÉTICO DE CuCo2InTe4 Y CuNi2InTe4)

Polycrystalline samples of nominal CuCo2InTe4 and CuNi2InTe4 were prepared by the melt and anneal method and the products characterized by powder X-ray diffraction and SQUID techniques. It was found that CuCo2InTe4 and CuNi2InTe4 crystallize in the tetragonal space group (Nº 121), Z = 2, in a stanni...

Resumen completo

Documentos citados

Guardado en:
Título de la revista: Revista Latinoamericana de Metalurgia y Materiales
Primer autor: Pedro Grima Gallardo
Otros autores: Miguel Soto;
Orlando Izarra;
Luis Nieves;
Miguel Quintero;
Gerzon E. Delgado;
Humberto Cabrera;
Inti Zumeta-Dubé;
Alejandro Rodríguez;
Jennifer R Glenn;
Jennifer A. Aitken
Palabras clave:
Nuevos Materiales; Semiconductores Semimagneticos; Magnetismo.;
Idioma: Español
Enlace del documento: http://www.rlmm.org/ojs/index.php/rlmm/article/view/761
Tipo de recurso: Documento de revista
Fuente: Revista Latinoamericana de Metalurgia y Materiales; Vol 37, No 1 (Año 2017).
Entidad editora: Universidad Simón Bolívar (Venezuela)
Materias: Ciencias Físicas e Ingeniería --> Ciencia de los Materiales, Cerámicas
Ciencias Físicas e Ingeniería --> Ciencia de los Materiales, Compuestos
Resumen: Polycrystalline samples of nominal CuCo2InTe4 and CuNi2InTe4 were prepared by the melt and anneal method and the products characterized by powder X-ray diffraction and SQUID techniques. It was found that CuCo2InTe4 and CuNi2InTe4 crystallize in the tetragonal space group (Nº 121), Z = 2, in a stannite-type structure, with the binaries CoTe and NiTe as secondary phases, respectively. The magnetic behavior of CuCo2InTe4 is that of a superparamagnetic state with an irreversibility temperature of ~450K and a maximum coercive field of 35 Oe at 2K; whereas CuNi2InTe4 shows two magnetic components, one diamagnetic an another weak ferromagnetic. Se prepararon muestras policristalinas de CuCo2InTe4 and CuNi2InTe4 en su valor nominal por el método de fusión y recocido, y los productos fueron caracterizados por las técnicas de difracción de rayos X y SQUID. Se encontró que CuCo2InTe4 and CuNi2InTe4 cristalizan en una estructura tetragonal, grupo espacial (Nº 121), Z = 2, tipo estannita, con presencia de los binarios CoTe y NiTe como fases secundarias, respectivamente. El comportamiento magnético de CuCo2InTe4 es de tipo superparamagnético con una temperatura de irreversibilidad de ~450K y un campo coercitivo máximo de 35 Oe a 2K; mientras que CuNi2InTe4 presenta dos componentes magnéticas, una diamagnética y otra ferromagnética débil.

Ejemplares similares