PHASE DIAGRAM OF (CuInTe2)1-x (FeTe) x ALLOYS (0 ≤ x ≤ 0.6)(DIAGRAMA DE FASES DEL SISTEMA DE ALEACIONES (CuInTe2)1-x (FeTe) x (0 ≤ x ≤ 0.6)

PHASE DIAGRAM OF (CuInTe2)1-x (FeTe) x ALLOYS (0 ≤ x ≤ 0.6)(DIAGRAMA DE FASES DEL SISTEMA DE ALEACIONES (CuInTe2)1-x (FeTe) x (0 ≤ x ≤ 0.6)

Polycrystalline samples of the (CuInTe2)1-x (FeTe)x alloy system where prepared by the melt and anneal technique and the products characterized by X-Ray Diffraction (XRD), Differential Thermal Analysis (DTA) and Optical Diffuse Reflectance Spectroscopy (ODRS) techniques. A first sight, samples were...

Resumo completo

Bibliografia

Guardado em:
Título da revista: Revista Latinoamericana de Metalurgia y Materiales
Primer autor: Pedro Grima-Gallardo
Outros autores: M. Quintero;
L. Nieves;
H. Cabrera;
E. Pérez-Cappé;
I. Zumeta-Dubé;
J. A. Aitken;
J. A. Brant
Palavras chave:
CuInTe2, FeTe, solid solutions, X-Ray Diffraction, Differential Thermal Analysis, Optical Diffuse Reflectance Spectroscopy, T-x Phase Diagram
Idioma: Espanhol
Ligação recurso: http://www.rlmm.org/ojs/index.php/rlmm/article/view/817
Tipo de recurso: Artigo de revista
Fonte: Revista Latinoamericana de Metalurgia y Materiales; Vol 38, No 1 (Ano 2018).
Entidade editora: Universidad Simón Bolívar (Venezuela)
Matérias: Ciências Físicas e Engenharia --> Ciência dos Materiais, Cerâmicas
Ciências Físicas e Engenharia --> Ciência dos Materiais, Compostos
Resumo: Polycrystalline samples of the (CuInTe2)1-x (FeTe)x alloy system where prepared by the melt and anneal technique and the products characterized by X-Ray Diffraction (XRD), Differential Thermal Analysis (DTA) and Optical Diffuse Reflectance Spectroscopy (ODRS) techniques. A first sight, samples were composed by a tetragonal phase with traces of a secondary phase identified as Fe1.125Te. Under exhaustive examination, it was found that the tetragonal phase, at the same time, is composed by two phases, with the same crystal structure and close lattice parameters, typical of spinodal decomposition. From ODRS measurements, optical absorption vs energy curves was obtained. These curves show how the addition of Fe produces a disordering-reordering process in the cationic sublattice suggesting that composition x=0.5 (CuFeInTe3) could be an intermediate compound in the diagram. Using the obtained information, a preliminary T-x phase diagram is proposed. Se prepararon muestras policristalinas del sistema de aleaciones (CuInTe2)1-x (FeTe)x por la técnica de fusión y recocido; los productos fueron caracterizados por las técnicas de Difracción de Rayos X (DRX), Análisis Térmico Diferencial (ATD) y Reflectancia por Espectroscopía de Óptica Difusa (REOD). A primera vista, las muestras se componen de una fase tetragonal con trazas de una fase secundaria identificada como Fe1.125Te. Bajo un examen más exhaustivo, se encontró que la fase tetragonal se compone a su vez de dos fases, con la misma estructura cristalina y parámetros de red cercanos, típico de una descomposición espinodal. A partir de mediciones REOD, se obtuvieron las curvas de absorción óptica vs energía. Estas curvas muestran cómo la adición de Fe produce un proceso de desorden-reorden en la subred catiónica que sugiere que la composición x = 0,5 (CuFeInTe3) podría ser un compuesto intermediario en el diagrama. Con la información obtenida, se propone un diagrama de fases T-x.