Effect of the polyacrylamide concentration on the quality of the copper deposit obtained by electrolytic refining
Effect of the polyacrylamide concentration on the quality of the copper deposit obtained by electrolytic refining
The effect of the additive non ionic polyacrylamide (PAM), was studied at the laboratory level, as refining crystalline grain in the copper electrorefining. Experiments were performed 24 h of electrolysis, using an electrolyte of copper sulphate acid, with 0.5 to 10 mgl-1 polyacrylamide at 55 °C and...
| Título traducido: | Efecto de la concentración de poliacrilamida sobre la calidad del depósito de cobre obtenido por refino electrolítico |
|---|---|
| Título de la revista: | Revista de Metalurgia |
| Primer autor: | J. Aragón |
| Otros autores: | J. Ipinza; J. Camus; A. Vargas; R. Saavedra |
| Palabras clave traducidas: | |
| Idioma: | No especificado |
| Enlace del documento: | http://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/1298 |
| Tipo de recurso: | Documento de revista |
| Fuente: | Revista de Metalurgia; Vol 49, No 6 (Año 2013). |
| DOI: | http://dx.doi.org/10.3989/revmetalm.1327 |
| Entidad editora: | Consejo Superior de Investigaciones Científicas CSIC |
| Derechos de uso: | Reconocimiento (by) |
| Materias: | Ciencias Físicas e Ingeniería --> Metalurgia e Ingeniería Metalúrgica |
| Resumen: | The effect of the additive non ionic polyacrylamide (PAM), was studied at the laboratory level, as refining crystalline grain in the copper electrorefining. Experiments were performed 24 h of electrolysis, using an electrolyte of copper sulphate acid, with 0.5 to 10 mgl-1 polyacrylamide at 55 °C and a current density of 260 Am-2. The effectiveness of these organic additives in copper electrorefining was determined by directly measuring the surface roughness of the copper deposit and contrasted with the results of other instrumental techniques (SEM and metallographic analysis). The results of the analysis SEM, metallographic analysis and measurement of the surface roughness of the copper deposit, show that to concentrations as low as 0.5 mgl-1 of this additive is manifested its property of tuner of grain. However, in the range of 7 to 10 mgl-1 of polyacrylamide, it reaches an optimum size of grain for the deposit of copper in the cathodes. |
|---|---|
| Resumen traducido: | El efecto del aditivo poliacrilamida no iónica (PAM), se estudió a nivel de laboratorio, como afinador de grano cristalino en el refino electrolítico del cobre. Se realizaron experimentos de electrólisis de 24 h, utilizando un electrolito de sulfato de cobre ácido, con 0,5 a 10 mgl-1 de poliacrilamida, a 55 °C y una densidad de corriente de 260 Am-2. La efectividad de este aditivo orgánico en la refinación electrolítica del cobre fue determinada mediante la medida de la rugosidad de la superficie del depósito de cobre y contrastada con los resultados de otras técnicas instrumentales (MEB y análisis metalográfico). Los resultados obtenidos del análisis MEB, análisis metalográfico y medición de la rugosidad superficial del depósito de cobre, muestran que a concentraciones tan bajas como 0,5 mgl-1 de este aditivo, se manifiesta su propiedad de afinador de grano. Sin embargo, en el rango de 7 a 10 mgl-1 de poliacrilamida, se alcanza un tamaño de grano óptimo para el depósito de cobre en el cátodo. |