Phase transformations in Zn-22%Al-2%Cu and Zn-22%Al-2%Cu-X (X = 1, 2 and 3%Ag) alloys during aging treatments
Phase transformations in Zn-22%Al-2%Cu and Zn-22%Al-2%Cu-X (X = 1, 2 and 3%Ag) alloys during aging treatments
The study of phase transformations that take place in Zn-22%Al-2%Cu and Zn-22%Al-2%Cu-X (X = 1, 2 and 3%Ag) alloys was carried out using X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). Alloys were homogenized at 350 °C during 10 days and quenched at ~2 °C. Subsequently, samples were...
| Título traducido: | Transformaciones de fase en aleaciones Zn-22%Al-2%Cu y Zn-22%Al-2%Cu-X (X = 1, 2 y 3%Ag) envejecidas isotérmicamente |
|---|---|
| Título de la revista: | Revista de Metalurgia |
| Primer autor: | Alfredo Flores-Ramos |
| Otros autores: | Héctor J. Dorantes-Rosales; Víctor M. López-Hirata; Felipe Hernández-Santiago; Jorge L. González-Velázquez; Alberto A. Torres-Castillo; Diego I. Rivas-López |
| Palabras clave traducidas: | |
| Idioma: | No especificado |
| Enlace del documento: | http://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/1335 |
| Tipo de recurso: | Documento de revista |
| Fuente: | Revista de Metalurgia; Vol 50, No 4 (Año 2014). |
| DOI: | http://dx.doi.org/10.3989/revmetalm.026 |
| Entidad editora: | Consejo Superior de Investigaciones Científicas CSIC |
| Derechos de uso: | Reconocimiento (by) |
| Materias: | Ciencias Físicas e Ingeniería --> Metalurgia e Ingeniería Metalúrgica |
| Resumen: | The study of phase transformations that take place in Zn-22%Al-2%Cu and Zn-22%Al-2%Cu-X (X = 1, 2 and 3%Ag) alloys was carried out using X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). Alloys were homogenized at 350 °C during 10 days and quenched at ~2 °C. Subsequently, samples were aged at 200 °C for different times. The initial microstructure consists in a matrix of fine equiaxial grains of α and η phases for all the alloys. Besides isolated particles of ε and Φ were observed without and with Ag addition, respectively. During the aging, the four phase reaction, α + ε→η + τ’, takes place to obtain the equilibrium η, α and τ’ phases. However, the Ag addition promotes the formation of the Φ phase, which retards or inhibits the four phase reaction. The stability of the Φ phase is obtained with 3%Ag, which could improve the dimensional stability of the alloy for future industrial applications. |
|---|---|
| Resumen traducido: | En el presente estudio sobre las transformaciones de fase en las aleaciones Zn-22%Al-2%Cu y Zn-22%Al-2%Cu-X (X = 1, 2 y 3%Ag) se utilizó Difracción de Rayos X (DRX) y Microscopía Electrónica de Barrido (MEB). Las aleaciones fueron homogeneizadas a 350 °C durante 10 días, templadas a ~2 °C y posteriormente envejecidas a 200 °C durante diferentes tiempos. Todas las aleaciones ensayadas presentaron una microestructura inicial formada por una matriz de granos finos y equiaxiales de las fases α y η. Además, para las aleaciones sin Ag se observa la presencia de partículas de la fase ε (CuZn4) y de Φ ((Ag, Cu) Zn4) en las que se adicionó Ag. Durante el envejecido, ocurre la reacción de cuatro fases, α + ε→η + τ’, para obtener las fases de equilibrio η, α y τ’. Sin embargo, la adición de Ag promueve la formación de la fase Φ, la cual retarda e incluso inhibe la reacción de cuatro fases. La estabilidad de la fase Φ se obtiene con 3%Ag, lo que podría mejorar la estabilidad dimensional de la aleación para futuras aplicaciones industriales. |